| Material | Rod Thickness | Rod Length | Color | Unit |
| %100 Virgin POM | 10 – 100 mm | 2000mm | Beige/White | Rod |
| Technical Specifications | |
| Density | 1,41 gr/cm³ |
| Tensile Strength | ≥ 66 Mpa |
| Max. Stretching | ≥ 50 Mpa |
| Working Temperatures Range | -50 °C - +140°C |
| Constant Working Temperature | 115/100 °C |
| Melting Temperature | 160°C |
| Electricity Resistance | 20Kv/mm |
| Impact Strength (without Notch) | 68 KJ/m² |
| Impact Strength (with Notch) | 8 KJ/m² |
| Material | Rod Thickness | Rod Length | Color | Unit |
| %100 Virgin POM | 10 – 100 mm | 2000mm | Beige/White | Rod |
| Technical Specifications | |
| Density | 1,41 gr/cm³ |
| Tensile Strength | ≥ 66 Mpa |
| Max. Stretching | ≥ 50 Mpa |
| Working Temperatures Range | -50 °C - +140°C |
| Constant Working Temperature | 115/100 °C |
| Melting Temperature | 160°C |
| Electricity Resistance | 20Kv/mm |
| Impact Strength (without Notch) | 68 KJ/m² |
| Impact Strength (with Notch) | 8 KJ/m² |
| Material | Rod Thickness | Rod Length | Color | Unit |
| %100 Virgin POM | 10 – 100 mm | 2000mm | Beige/White | Rod |
| Technical Specifications | |
| Density | 1,41 gr/cm³ |
| Tensile Strength | ≥ 66 Mpa |
| Max. Stretching | ≥ 50 Mpa |
| Working Temperatures Range | -50 °C - +140°C |
| Constant Working Temperature | 115/100 °C |
| Melting Temperature | 160°C |
| Electricity Resistance | 20Kv/mm |
| Impact Strength (without Notch) | 68 KJ/m² |
| Impact Strength (with Notch) | 8 KJ/m² |
| Material | Rod Thickness | Rod Length | Color | Unit |
| %100 Virgin POM | 10 – 100 mm | 2000mm | Beige/White | Rod |
| Technical Specifications | |
| Density | 1,41 gr/cm³ |
| Tensile Strength | ≥ 66 Mpa |
| Max. Stretching | ≥ 50 Mpa |
| Working Temperatures Range | -50 °C - +140°C |
| Constant Working Temperature | 115/100 °C |
| Melting Temperature | 160°C |
| Electricity Resistance | 20Kv/mm |
| Impact Strength (without Notch) | 68 KJ/m² |
| Impact Strength (with Notch) | 8 KJ/m² |