| Model | Sheet Thickness | Sheet Size | Color | Unit |
| HP2061 | 0,50 - 22 mm | 1000 x 2000 mm | Brown | Sheet |
| Technical Specifications | Standard | Test Result |
| Bending elastic modulus of appearance | min 2800 Mpa | 3400 Mpa |
| Compressive Strength flexural to laminations | min120 Mpa | 133 Mpa |
| Peel Strength (parallel laminations) | min 4 Mpa | 4.3 Mpa |
| Tensile Strength | min 40 Mpa | 47 Mpa |
| Density | 1.3-1.4 g/cm³ | 1.38g/cm³ |
| Model | Sheet Thickness | Sheet Size | Color | Unit |
| HP2061 | 0,50 - 22 mm | 1000 x 2000 mm | Brown | Sheet |
| Technical Specifications | Standard | Test Result |
| Bending elastic modulus of appearance | min 2800 Mpa | 3400 Mpa |
| Compressive Strength flexural to laminations | min120 Mpa | 133 Mpa |
| Peel Strength (parallel laminations) | min 4 Mpa | 4.3 Mpa |
| Tensile Strength | min 40 Mpa | 47 Mpa |
| Density | 1.3-1.4 g/cm³ | 1.38g/cm³ |
| Model | Sheet Thickness | Sheet Size | Color | Unit |
| HP2061 | 0,50 - 22 mm | 1000 x 2000 mm | Brown | Sheet |
| Technical Specifications | Standard | Test Result |
| Bending elastic modulus of appearance | min 2800 Mpa | 3400 Mpa |
| Compressive Strength flexural to laminations | min120 Mpa | 133 Mpa |
| Peel Strength (parallel laminations) | min 4 Mpa | 4.3 Mpa |
| Tensile Strength | min 40 Mpa | 47 Mpa |
| Density | 1.3-1.4 g/cm³ | 1.38g/cm³ |
| Model | Sheet Thickness | Sheet Size | Color | Unit |
| HP2061 | 0,50 - 22 mm | 1000 x 2000 mm | Brown | Sheet |
| Technical Specifications | Standard | Test Result |
| Bending elastic modulus of appearance | min 2800 Mpa | 3400 Mpa |
| Compressive Strength flexural to laminations | min120 Mpa | 133 Mpa |
| Peel Strength (parallel laminations) | min 4 Mpa | 4.3 Mpa |
| Tensile Strength | min 40 Mpa | 47 Mpa |
| Density | 1.3-1.4 g/cm³ | 1.38g/cm³ |